Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX674PC - Europe - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

NORYL GTX™ 674PC resin is a conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for in- or on-line primer-less powder coat painting around corners and holes with a Class A Surface. NORYL GTX674PC resin exhibits high heat resistance, improved surface appearance and is an excellent candidate for automotive applications such as mirror housings and brackets. This material is only available in black.

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
溶融時の密度	967	kg/m³	-
溶融時の熱伝導率	0.19	W/(m K)	-
溶融時の比熱	3760	J/(kg K)	-
突き出し時の時の温度	156	°C	-
ASTM数据
メルトフローレイト, MFI	25	g/10min	ASTM D 1238
温度	300	°C	-
荷重	5	kg	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	2320	MPa	ISO 527
降伏ひずみ	3	%	ISO 527
破壊応力	60	MPa	ISO 527
破壊ひずみ	4	%	ISO 527
曲げ弾性率	2480	MPa	ISO 178
ASTM数据
引張弾性率	2810	MPa	ASTM D 638
降伏応力	65	MPa	ASTM D 638
破壊応力	64	MPa	ASTM D 638
降伏点伸び	3	%	ASTM D 638
破断伸び	4	%	ASTM D 638
曲げ弾性率	2890	MPa	ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in	74	J/m	ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature	50	J/m	ASTM D 256
温度	-30	°C	-

熱的特性	値	単位	テスト基準
ISO データ
荷重たわみ温度, 0.45 MPa	185	°C	ISO 75-1/-2
ビカット軟化温度, B	197	°C	ISO 306
ビカット軟化温度, 120°C/h 50N	196	°C	ISO 306
線膨張係数, 平行	122	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	134	E-6/K	ISO 11359-1/-2
ASTM数据
DTUL @ 66 psi	188	°C	ASTM D 648
ビカット軟化温度	197	°C	ASTM D 1525

その他の特性.	値	単位	テスト基準
密度.	1110	kg/m³	ISO 1183
密度	1110	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	95 - 105	°C	-
Pre-drying - Time	3 - 4	h	-
Processing humidity	≤0.07	%	-
樹脂温度	280 - 305	°C	-
金型温度	75 - 120	°C	-
Zone 1	265 - 305	°C	-
Zone 2	270 - 305	°C	-
Zone 3	275 - 305	°C	-
Screw speed	20 - 100	rpm	-
Back pressure	0.3 - 1.4	MPa	-

機能

特殊な特性

成形加工法.

射出成形.

領域別の利用可能性

ヨーロッパ.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.